지르코늄 산화물 및 지르코늄계 혼합 산화물의 제조 방법

Abstract

This invention relates to a process for preparing zirconium oxide, in its various forms, including zirconium-based mixed oxides. There is described a process for preparing a zirconium oxide in the absence of a cerium salt which comprises precipitating a zirconium hydroxide from an aqueous solution of a zirconium salt by reaction with an alkali in the presence of a controlled amount of sulphate anions at a temperature not greater than 50°C and then calcining the hydroxide to form an oxide, wherein the oxide thus formed is essentially sulphate free. Catalysts and ceramics can be produced from the product oxides having improved thermal stability and improved sinterability, respectively. A particular use of the product oxide is as a promoter or catalyst support in automobile exhaust systems.
본 발명은 지르코늄 산화물을 이의 다양한 형태(지르코늄계 혼합 산화물을 포함함)로 제조하는 방법에 관한 것이다. 상기 방법은 세륨 염의 부재하에 지르코늄 산화물을 제조하는 방법을 기술하고 있으며, 50 ℃ 이하의 온도에서 조절된 양의 설페이트 음이온의 존재하에서의 알칼리와의 반응에 의해 지르코늄 염 수용액으로부터 지르코늄 수산화물을 침전시키는 단계와; 상기 지르코늄 수산화물을 하소시켜서 산화물을 형성시키는 단계(이와 같이 형성된 산화물은 본질적으로 설페이트를 함유하지 않음)를 포함한다. 촉매 및 세라믹은 각각 개선된 열안정성과 개선된 소결성을 갖는 생성된 산화물로부터 제조될 수 있다. 생성된 산화물은 자동차 배기 시스템에서 촉진제 또는 촉매 지지체로서 사용되는 것을 특징으로 한다.

Claims

Description

Topics

Download Full PDF Version (Non-Commercial Use)